Páska z nerezové oceli 321
Dodávka plechu z nerezové oceli třídy Baogu
| Typ | Školní známka | Školní známka | Chemická složka % | ||||||||||
| C | Cr | Ni | Mn | P | S | Mo | Si | Cu | N | jiný | |||
| austenitické | 201 | SUS201 | ≤0,15 | 16:00-18:00 | 3,50-5,50 | 5,50 – 7,50 | ≤0,060 | ≤0,030 | - | ≤1,00 | - | ≤0,25 | - |
| 202 | SUS202 | ≤0,15 | 17:00-19:00 | 4:00-6:00 | 7,50-10,00 | ≤0,060 | ≤0,030 | ≤1,00 | - | ≤0,25 | - | ||
| 301 | 1,431 | ≤0,15 | 16:00-18:00 | 6:00-8:00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | ≤0,10 | - | |
| 304 | 1,4301 | ≤0,07 | 17:00-19:00 | 8:00-10:00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 304 l | 1,4307 | ≤0,030 | 18:00-20:00 | 8:00-10:00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 304H | 1,4948 | 0,04-0,10 | 18:00-20:00 | 8:00-10:00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 309 | 1,4828 | ≤0,20 | 22:00-24:00 | 12:00-15:00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 309S | * | ≤0,08 | 22:00-24:00 | 12:00-15:00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 310 | 1,4842 | ≤0,25 | 24:00-26:00 | 19:00-22:00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 310S | * | ≤0,08 | 24:00-26:00 | 19:00-22:00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,50 | - | - | - | |
| 314 | 1,4841 | ≤0,25 | 23:00-26:00 | 19:00-22:00 | ≤2,00 | ≤0,045 | ≤0,030 | - | 1,50-3,00 | - | - | - | |
| 316 | 1,4401 | ≤0,08 | 16:00-18:50 | 10:00-14:00 | ≤2,00 | ≤0,045 | ≤0,030 | 2:00-3:00 | ≤1,00 | - | - | - | |
| 316L | 1,4404 | ≤0,030 | 16:00-18:00 | 10:00-14:00 | ≤2,00 | ≤0,045 | ≤0,030 | 2:00-3:00 | ≤1,00 | - | - | - | |
| 316Ti | 1,4571 | ≤0,08 | 16:00-18:00 | 10:00-14:00 | ≤2,00 | ≤0,045 | ≤0,030 | 2:00-3:00 | ≤1,00 | - | 0,1 | Ti5(C+N)~0,70 | |
| 317 | * | ≤0,08 | 18:00-20:00 | 11:00-15:00 | ≤2,00 | ≤0,045 | ≤0,030 | 3:00-4:00 | ≤1,00 | - | 0,1 | - | |
| 317L | 1,4438 | ≤0,03 | 18:00-20:00 | 11:00-15:00 | ≤2,00 | ≤0,045 | ≤0,030 | 3:00-4:00 | ≤1,00 | - | 0,1 | - | |
| 321 | 1,4541 | ≤0,08 | 17:00-19:00 | 9:00-12:00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Ti5(C+N)~0,70 | |
| 321H | * | 0,04-0,10 | 17:00-19:00 | 9:00-12:00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Ti5(C+N)~0,70 | |
| 347 | 1,455 | ≤0,08 | 17:00-19:00 | 9:00-12:00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Nb>10*C%-1,10 | |
| 347H | 1,494 | 0,04-0,10 | 17:00-19:00 | 9:00-12:00 | ≤2,00 | ≤0,045 | ≤0,030 | - | ≤1,00 | - | - | Nb>10*C%-1,10 | |
| xm-19 | Nitronic50 | ≤0,06 | 20:50-23:50 | 11.50-13.50 | 4,0-6,0 | ≤0,045 | ≤0,030 | 1,50-3,00 | ≤1,00 | - | 0,2-0,4 | Nb:0,10-0,30 V:0,10-0,30 | |
| 904L | N08904 | ≤0,02 | 19,0-23,0 | 23,0-28,0 | 4,0-5,0 | ≤0,045 | ≤0,035 | ≤1,00 | 0,1 | Cu: 1,0-2,0 | |||
| Duplex | 2205 | S32205 | ≤0,03 | 22,0-23,0 | 4,5-6,5 | ≤2,00 | ≤0,030 | ≤0,020 | 3,0-3,5 | ≤1,00 | - | 0,14-0,20 | |
| 2507 | S32750 | ≤0,03 | 24,0-26,0 | 6,0-8,0 | ≤1,20 | ≤0,035 | ≤0,020 | 3,0-5,0 | ≤0,80 | 0,5 | 0,24-0,32 | ||
| * | S32760 | ≤0,03 | 24,0-26,0 | 6,0-8,0 | ≤1,00 | ≤0,030 | ≤0,010 | 3,0-4,0 | ≤1,00 | 0,5-1,00 | 0,2-0,3 | ||
| 2304 | S32304 | ≤0,03 | 21,5-24,5 | 3,0-5,5 | ≤2,50 | ≤0,040 | ≤0,030 | 0,05-0,6 | ≤1,00 | 0,05-0,6 | 0,05-0,2 | ||
| 329 | 1,446 | ≤0,08 | 23:00-28:00 | 2,00-5,00 | ≤1,00 | ≤0,040 | ≤0,030 | 1,00-2,00 | ≤0,75 | - | - | ||
| Ferit | 409 | S40900 | ≤0,03 | 10,50-11,70 | 0,5 | ≤1,00 | ≤0,040 | ≤0,020 | - | ≤1,00 | - | ≤0,030 | Ti6(C+N)~0,50 Nb:0,17 |
| 430 | 1Cr17 | ≤0,12 | 16:00-18:00 | - | ≤1,0 | ≤0,040 | ≤0,030 | - | ≤1,0 | - | - | - | |
| 444 | S44400 | ≤0,025 | 17:50-19:50 | 1 | ≤1,00 | ≤0,040 | ≤0,030 | 1,75-2,5 | ≤1,00 | - | 0,035 | Ti+Nb:0,2+4(C+N)~0,80 | |
| 446 | S44600 | ≤0,20 | 23:00-27:00 | 0,75 | ≤1,5 | ≤0,040 | ≤0,030 | 1,50-2,50 | ≤1,00 | - | ≤0,25 | - | |
| Martenzit | 410 | 1Cr13 | 0,08-0,15 | 11.50-13.50 | 0,75 | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - |
| 410S | * | ≤0,080 | 11.50-13.50 | 0,6 | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 416 | Y1Cr13 | ≤0,15 | 12:00-14:00 | 3) | ≤1,25 | ≤0,060 | ≥0,15 | - | ≤1,00 | - | - | - | |
| 420 | 2Cr13 | ≥0,15 | 12:00-14:00 | - | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 420J2 | 3Cr13 | 0,26-0,35 | 12:00-14:00 | - | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤1,00 | - | - | - | |
| 431 | 1Cr17Ni2 | ≤0,20 | 15:00-17:00 | 1,50-2,50 | ≤1,00 | ≤0,040 | ≤0,030 | - | ≤0,80 | - | - | - | |
| 440C | 11Cr17 | 0,95-1,20 | 16:00-18:00 | - | ≤1,00 | ≤0,040 | ≤0,030 | 0,75 | ≤1,00 | - | - | - | |
| PH | 630 | 17-4PH | ≤0,07 | 15:00-17:50 | 3,00-5,00 | ≤1,00 | ≤0,035 | ≤0,030 | - | ≤1,00 | 3,00-5,00 | - | Nb 0,15-0,45 |
| 631 | 17-7 PH | ≤0,09 | 16:00-18:00 | 6,50-7,50 | ≤1,00 | ≤0,035 | ≤0,030 | - | ≤1,00 | ≤0,50 | - | Al 0,75-1,50 | |
| 632 | 15-5PH | ≤0,09 | 14:00-16:00 | 3,50-5,50 | ≤1,00 | ≤0,040 | ≤0,030 | 2:00-3:00 | ≤1,00 | 2,5-4,5 | - | Al 0,75-1,50 | |
Popis
Pás z nerezové oceli 321 je druh austenitické nerezové oceli s nízkým obsahem uhlíku a dobrou odolností proti korozi v mnoha korozivních prostředích.321 nabízí vynikající svařitelnost, dobrou obrobitelnost a vynikající zpracovatelské vlastnosti.
Pás z nerezové oceli 321 se běžně používá v chemickém průmyslu, celulózovém a papírenském průmyslu, námořním a pobřežním strojírenství a také v potravinářském a nápojovém průmyslu.
Pás z nerezové oceli 321 má také vysokou úroveň odolnosti proti praskání chloridovou korozí a důlkové korozi.Je také odolný vůči kyselině chlorovodíkové při zvýšených teplotách až do 250 °C (480 °F).
Funkce
Dobrá odolnost proti korozi: Pás z nerezové oceli 321 má lepší odolnost proti korozi než typy nerezových ocelí 304 a 316, díky čemuž je ideální pro použití v korozivním prostředí.
Vynikající svařitelnost: Pás z nerezové oceli 321 lze svařovat všemi metodami včetně obloukového svařování ( TIG / GTAW ), svařování elektronovým paprskem ( EBW / EFW ), svařování pod tavidlem ( SAW ) a svařování laserovým paprskem ( LBIW ).
Vysoká pevnost: Úrovně pevnosti pásku z nerezové oceli 321 jsou až o 50 % vyšší než u typů nerezových ocelí 304 a až o 80 % vyšší než u 316 typů nerezových ocelí kvůli jejich zvýšenému obsahu uhlíku a velikosti zrna austenitu.